What is the density of 316?

8000 kg/m³ — the figure the weight calculators on this site use for 316. The value is Outokumpu / stainless technical resources’s.

What is the chemical composition of 316?

C ≤ 0.08, Si ≤ 0.75, Mn ≤ 2, P ≤ 0.045, S ≤ 0.03, Cr 16–18, Ni 10–14, Mo 2–3, N ≤ 0.1, in mass %, to ASTM A240. An element the standard sets no requirement for is left blank here rather than written as zero.

What are the mechanical properties of 316?

Tensile ≥ 515 MPa, Yield ≥ 205 MPa, Elongation min ≥ 40 % — ASTM A240, Plate/Sheet/Strip, Annealed. Those are the standard’s requirements; the mill test certificate governs the metal delivered.

316 — properties and composition — Hidayath Metal Industries

Designations

UNS: S31600
EN number: 1.4401
EN name: X5CrNiMo17-12-2
AISI: 316

Density

Density: 8000 kg/m³
Per: Outokumpu / stainless technical resources
Corrosion resistance: Very good
Product forms: Sheet, plate, pipe, tube, bar

Chemical composition

Chemical composition — mass %
Standard	Product form	Basis	C	Si	Mn	P	S	Cr	Ni	Mo	N
ASTM A240	Plate/Sheet/Strip	Specification	≤ 0.08	≤ 0.75	≤ 2	≤ 0.045	≤ 0.03	16–18	10–14	2–3	≤ 0.1

mass %. A blank cell means the standard sets no requirement for that element, not zero. Single values are limits: "≤" a maximum, "≥" a minimum.

Reference values from the cited standards. They describe what the standard requires, not a specific heat of material; the mill test certificate governs what is delivered.

Mechanical properties

Mechanical properties
Standard	Product form	Condition / temper	Thickness	Test temperature	Yield	Tensile	Elongation min	Hardness max	Notes
ASTM A240	Plate/Sheet/Strip	Annealed	–	20 °C	0.2% offset ≥ 205 MPa	≥ 515 MPa	40 % (2 in / 50 mm gauge basis (product dependent))	95 HRB	Minimum values.
EN 10088-2	Flat products	Solution annealed	≤ 75 mm	20 °C	Rp0.2 ≥ 220 MPa	520–670 MPa	40 % (A (thickness/product dependent))	–	Representative EN flat-product range.

Each row is one standard, one product form and one condition — the values do not transfer across rows. A blank cell means the standard sets no requirement.

Reference values from the cited standards. They describe what the standard requires, not a specific heat of material; the mill test certificate governs what is delivered.

Typical applications

Marine, chemical, food, architectural

Approximate equivalents

Approximate equivalents: equivalents are a technical reference, not a substitution instruction, verify against project specification.

Approximate equivalents
Grade	Systems	Relationship	Note	Key difference
316	ASTM/AISI/UNS → EN	Same grade, another designation	Commonly cross-referenced designation.	Mechanical/chemistry limits vary by standard/product. Compared designation: 1.4401 / X5CrNiMo17-12-2.

Common questions

01What is the density of 316?: 8000 kg/m³ — the figure the weight calculators on this site use for 316. The value is Outokumpu / stainless technical resources’s.
02What is the chemical composition of 316?: C ≤ 0.08, Si ≤ 0.75, Mn ≤ 2, P ≤ 0.045, S ≤ 0.03, Cr 16–18, Ni 10–14, Mo 2–3, N ≤ 0.1, in mass %, to ASTM A240. An element the standard sets no requirement for is left blank here rather than written as zero.
03What are the mechanical properties of 316?: Tensile ≥ 515 MPa, Yield ≥ 205 MPa, Elongation min ≥ 40 % — ASTM A240, Plate/Sheet/Strip, Annealed. Those are the standard’s requirements; the mill test certificate governs the metal delivered.
04What is 316 used for?: Marine, chemical, food, architectural